lft-g PA66 nylon66 remplissage fibre de carbone longue 20%-60% plastique modifié haute performance couleur naturelle

Material Introduction

In 1935, Wallace Carothers, a scientific researcher at DuPont, and his team successfully synthesized PA66 by condensation of adipic acid and adipic diamine for the first time, and DuPont completed the commercial production of PA66 fiber in 1939.

Starting in the 1950s, PA, including PA6 and PA66, was developed for the production of injection molded products to replace metal to meet the requirements of light weight and cost reduction of industrial products.

At present, PA66 is the most used PA species other than PA6.

PA66
Scientific name: Polyhexanediamide
Abbreviation: PA66
Common name: Nylon 66 

PA66 has many similarities with PA6. PA66 is also a transparent to milky white granule that can take on almost any color with the addition of a colorant (masterbatch) specific for polymers.

Material properties

Similar to the basic properties of PA6, PA66 also has low specific gravity, high tensile strength, wear resistance, good self-lubrication, and excellent impact toughness.

In addition, because the number of hydrogen bonds in PA66 is more than in PA6, the intermolecular force of PA66 is stronger than the intermolecular force of PA6, which makes the internal structure of PA66 more compact than PA6, with better thermal properties, higher rigidity and toughness, better dimensional stability, lower water absorption, and more wear resistance.

However, PA66 has a higher market price than PA6 and is not as easy to process and mold as PA6.

Like PA6, PA66 can also add a certain percentage of glass fiber, carbon fiber, etc. to improve the performance and meet the application needs of different products.

The following table is a PA66-LCF30 performance table produced by Xiamen LFT composite plastic company.

Materials Application

PA66 has higher hardness, mechanical strength, toughness, self-lubrication, friction resistance, heat resistance after the addition of carbon fiber, and is widely used in automotive parts, electrical and electronic, as well as mechanical and engineering parts and other fields.

Automotive parts

PA66's low specific gravity, high rigidity, strong toughness, heat resistance and gasoline resistance make it widely used in automotive modules, automotive structural parts, automotive interior and exterior parts, automotive transmission system and chassis shield, automotive fuel system, automotive ignition system, etc. The products involve automotive cable channel modules, structural parts of front-end components of automotive sunroof system, automotive rearview mirror bracket, automotive radiator, headlight support frame, door module, seat structural parts, seat shell and backrest, dashboard skeleton, air cooler fan, etc.

Electrical and electronics
PA66's good insulation, flame retardancy and corrosion resistance make it suitable for making various connectors, switches, sockets, terminal blocks, wire coverings, wire ties, insulating spacers, circuit breaker housings, transformer bobbins, retaining clips and motor parts after glass fiber reinforcement.

Mechanical and engineering parts
PA66's good rigidity, toughness, self-lubricating properties, heat and abrasion resistance make it suitable for manufacturing various nuts, screws, cable ties, worm gears, rotating wheels, gears, pump impellers, pulley sleeves, bushings, solenoid distribution valve seats, power tool housings, pipes, luggage racks, fan housings, appliance housings, door and window frames, cable drag chains and large machine tool baffles.

Details

D'autres produits que vous vous demandez peut-être

                 pa6-lcf                                     pa 12 -lcf                                   p e e k-lcf

Questions fréquemment posées

Q. Comment choisir la méthode de renforcement et la longueur du matériau lors de l'utilisation d'un matériau thermoplastique renforcé de fibres longues ?

A. La sélection des matériaux dépend des exigences des produits. Il est nécessaire de déterminer dans quelle mesure le contenu est amélioré et dans quelle mesure la longueur est plus appropriée, qui dépendent des exigences de performance des produits.

Q. Dans quelles circonstances la fibre longue peut-elle remplacer la fibre courte ? Quels sont les matériaux alternatifs courants ?

A. Les matériaux traditionnels en fibres discontinues peuvent être remplacés par des matériaux LFT en fibre de verre longue et en fibre de carbone longue dans le cas de clients dont les propriétés mécaniques ne peuvent pas être satisfaites ou lorsque des substituts métalliques plus élevés sont souhaités. Par exemple, la fibre de verre longue PP remplace souvent la fibre de verre renforcée de nylon et la fibre de verre longue nylon remplace la série PPS.

Q. Existe-t-il des exigences de processus spéciales pour les fibres de carbone longues pour les produits de moulage par injection ?

A. Nous devons tenir compte des exigences de la fibre de carbone longue pour la buse à vis de la machine de moulage par injection,  la structure du moule et le processus de moulage par injection.  La fibre de carbone longue est un matériau relativement coûteux et doit évaluer le coût du problème de performance dans le processus de sélection.